Inert Ceramic Ball 1/4 inch
Professional manufactor for inert ceramic ball , alumina ceramic ball, Refractory ball and all kinds of water treatment ceramic ball.
Inert ceramic balls used as covering and supporting materials of catalysts in reaction vessels and as packing in towers, are widely used in petroleum, chemical engineering, fertilizer production, natural gas and environmental protection.
Introduction: Ceramic balls are widely used support media in the world because of their excellent consistence and reliability. Products to these specifications are manufactured from very high quality chemical-porcelain clay materials, which has quite excellent stability, high mechanical strengthand resistance to thermal shock. This makes them all ideal choice for support of all types of catalyst.
Chemical composition & Physical properties
Specification | Common Ceramic Ball | Inert Ceramic Ball | Medium Alumina Ball | High Alumina Ball | 99% Alumina Ball |
Al2O3 + SiO2 (%) | >93 | >92 | >93 | >94 | >99 |
Al2O3 (%) | 17-23 | 23-30 | 47-56 | 90-93 | 99 |
Fe2O3 (%) | <1 | <1 | <1 | <1 | <1 |
CaO (%) | <0.5 | <1.5 | <2 | <4 | 0.2 |
MgO (%) | <0.5 | <2.5 | <0.5 | <0.5 | 0.1 |
K2O + Na2O (%) | <4 | <4 | <3.5 | <4 | >0.5 |
TiO2 |
| <0.5 | <0.1 | <0.1 | 0.5 |
Leachable Iron (%) |
| <0.1 | <0.001 | <0.001 |
|
Water Absorption (%) | <0.5 | <0.2 | <2 | <3 | 2.0-6.0 |
Bulk Density (g/cm3) | 1.35-1.40 | 1.35-1.40 | 1.35-1.45 | 1.8-2.0 | 1.8-2.0 |
Operation Temp. max. | >1100 | >1100 | 1480 | 1760 |
|
Mohs Hardness (scale) | >6.5 | >7 | >7 | >7 | >7.5 |
Crush Strength | KN/particle | ||||
1/4 inch (6mm) | >0.5 | >0.54 | >0.56 | >0.44 | >1 |
1/2 inch (13mm) | >1.5 | >1.67 | >1.56 | >1.99 | >3 |
3/4 inch (19mm) | >4.15 | >4.21 | >2.89 | >3.21 | >5 |
1 inch (25mm) | >6.07 | >6.22 | >4.89 | >5.33 | >8 |
1-1/2 inch (38mm) | >8.52 | >8.92 | >5.33 | >5.28 | >8 |
2 inch (50mm) | >9.7 | >9.8 | >6.22 | >8 | >15 |
Chemical composition
| Typical Technical Composition | Min. % | Max. % | Usual % |
SiO2 | 64.00 | 75.00 | 68.40 |
Al2O3 | 19.00 | 26.00 | 24.50 |
Fe2O3 | ****** | 1.60 | 0.94 |
TiO2 | ****** | 1.40 | 0.96 |
CaO | ****** | 0.65 | 0.42 |
MgO | ****** | 0.60 | 0.38 |
Na2O | ****** | 2.00 | 1.12 |
K2O | ****** | 3.50 | 3.28 |
Al2O3 + SiO2 | 90.00 | 96.00 | 92.90 |
Physical properties
| Index | Value | Value |
Leachable Iron | ≤ 0.1% | ****** |
Apparent Porosity by Weight, dia. ≥ 10mm | ≤ 0.4% | ****** |
Apparent Porosity by Weight, dia. = 6mm | ≤ 1.0% | ****** |
Apparent Porosity by Weight, dia. = 3mm | ≤ 3.0% | ****** |
Moh's Hardness Scale | >6.5 | ****** |
Water Absorption | <1.0wt.% | ****** |
Acid Resistance | >99.8% | ****** |
Thermal Conductivity | 0.9-1.0 w/m 2 .k | ****** |
Thermal Expansion @ 500 | 0.20% | ****** |
Specific Heat | 628-837 j/kgq | ****** |
Thermal Shock Stability, 500 then water cooling | 10 times | ****** |
Max. Operating Temperature | 1050 | 1922 |
Specific Density | 2,300 kg /m 3 | 144 lb /ft 3 |
Bulk Density (Packing Density) | 1,350 g /cm 3 | 84 lb /ft 3 |
Crush Strength
| Size / | Crush Strength | |||
Nominal Size | (lbs) | (kg) | (N/pc) | |
mm | Inch | min. | min. | min. |
3 | 1/8 | 50 | 23 | 225 |
6 | 1/4 | 123 | 56 | 550 |
10 | 3/8 | 202 | 92 | 902 |
13 | 1/2 | 385 | 175 | 1716 |
16 | 5/8 | 520 | 236 | 2315 |
19 | 3/4 | 978 | 444 | 4355 |
25 | 1 | 1428 | 648 | 6355 |
38 | 1-1/2 | 2020 | 916 | 8983 |
50 | 2 | 2987 | 1355 | 13288 |
Inert Ceramic Ball 1/4 inch